When the initial rotational speed increases to 6500r/min, the friction factor of the Cu-modified CFC-SiC decreases to 0.24

The line wear rate of Cu modified CFC-SiC itself and the dual parts is increased to 1.87μm/(face*turn) and 1.68μm/(face*turn) respectively. The above values are all lower than those of the typical CFC-SiC friction materials.

It shows that the Cu modified CFC-SiC friction material has excellent friction resistance and friction reduction effect, and it is more significant at low speed conditions.