After being oxidized at 700℃ in static air for 66 hours, the weight loss rate of phosphate-coated CFC is only 1.11%.

After being oxidized at 1200℃ for 5 minutes, the weight loss rate of phosphate-coated CFC is less than 0.8%.

After 100 thermal cycles from 900℃ to room temperature, the weight loss rate of phosphate-coated CFC is no more than 1.6%.